LA PROBETA COMPACTA CON DOBLE ENTALLA (PCDE) PARA EL ESTUDIO DE LA ROTURA DEL HORMIGON POR TENSIONES TANGENCIALES: ESTUDIO EXPERIMENTAL

THE DOUBLE-EDGE NOTCHET SPECIMEN (DENS) APPLIED TO STUDY THE FRACTURE OF CONCRETE UNDER SHEAR LOADING: EXPERIMENTAL APPROACH

El articulo presenta los resultados exprimentales de la campana realizada para verificar la validez de la geometria de la Probeta Compacta con Doble Entalla (PCDE) en el estudio de la rotura del hormigon bajo tensiones tangenciales (modo II). Los ensayos se han realizado con probetas de hormigon de tres tamanos y con probetas de PoliMetilMetacrilato (PMMA). Se presentan los detalles de la investigacion, en especial las tecnicas empleadas para la deteccion y seguimiento de las grietas debidas a las tensiones tangenciales, asi como a los registro experimentales de las variables medidas durante los ensayos. Los resultados obtenidos ponen de manifiesto que la rotura se inicia bajo fuertes tensiones tangenciales (modo II importante) pero que, superada la fase de inicio de la rotura, las grietas se propagan debido a las tensiones de traccion locales (modo I, local). (A). Resumen en ingles: The Double-Edge Notchet Specimen (DENS) under compression loading has been recently proposed by Reinhardt to study the fracture of concrete under tangential stresses. The testing procedure was successful with highly orthotropic materials, but some doubts remain about its applicability to mortar and concrete, particularly to evaluate mode II fracture energy. This paper shows the experimental set up and measurements devoted to check the suitability of this testing procedure for analysing de fractues of concrete under shear loading (mode II). Tests were performed with concrete speciments (three sizes) and PolyMethyMethacrylate (PMMA). The paper presents the experimental details, especially the procedures to detect and follow the starting and growing of the cracks. The experimental records are also shown. The results show that the fracture of concrete starts under high tangential stresses (mode II), but, after this inistial phase, the cracks grow under predominant tensile stresses (mode I). (A).

  • Authors:
    • CENDON FRANCO, D A
    • GALVEZ RUIZ, J C
    • ELICES CALAFAT, M
  • Publication Date: 2003-1

Language

  • Spanish

Media Info

  • Pagination: 89-102
  • Serial:

Subject/Index Terms

Filing Info

  • Accession Number: 01204707
  • Record Type: Publication
  • Source Agency: Centro de Estudios y Experimentación de Obras Públicas (CEDEX)
  • Files: ITRD
  • Created Date: Oct 7 2010 8:06PM