INFLUENCE OF THE LOWEST TEMPERATURE OF FREEZING, CONCENTRATION OF DEICER (SODIUM CHLORIDE) AND MIX PROPORTION OF MORTAR ON SALT SCALING DETERIORATION OF CONCRETE

ソルトスケーリングにおよぼす冷却最低温度と凍結防止剤濃度及びモルタル配合の影響

Concrete deterioration due to scaling of surface became harder with increase of scattering deicer (sodium chloride) for concrete road structure. This kind of deterioration is well known as salt scaling of concrete. Recently the authors' laboratory proposed new test method with small sized sample which has a good correlation between ASTM C 672 and other test methods. With using this test method, influence of the lowest temperature of freezing, concentration of deicer (sodium chloride) and mix proportion of mortar on salt scaling deterioration of concrete are studied in this research. There is no appearance of scaling deterioration in case of using pure water at any lowest temperature of freezing. Salt scaling of concrete was more generated under deicer concentration of 0.1% to 10%, and -7 degree centigrade or lower of lowest temperature of freezing. Water cement ratio of less than 0.25 is effective to decrease salt scaling. Sand cement ratio from 1 to 3 is not effective.NaCl等の凍結防止剤の使用に伴いコンクリートのスケーリング劣化が激しくなっており、この現象をソルトスケーリングという。ここではスケーリング劣化現象を解明するため、ASTM C 672法と整合性がある本研究室で開発した小片試験方法を使用し、ソルトスケーリングに及ぼす冷却最低温度(0~-40℃)及び凍結防止剤の濃度の影響(0.01-10%)を把握した。さらにモルタルの配合の影響を把握するため、砂セメント比(S/C=0-3)及び水セメント比(W/C=0.25-0.7)をかえてソルトスケーリングを評価した。ソルトスケーリングは真水では起こらず、幅広い凍結防止剤の濃度(0.1-10%)で生じる。凍結する最低温度の影響は少なく、-7℃以下の温度で生じる。砂セメント比は著しく小さい場合、水セメント比も0.35以下で抑制効果があるが、それ以上では水セメント比の影響は少なく、砂セメント比が1以下の範囲では抑制されるが、それ以上では影響は少ない。

Language

  • English
  • Japanese

Media Info

Subject/Index Terms

Filing Info

  • Accession Number: 01597025
  • Record Type: Publication
  • Source Agency: Japan Science and Technology Agency (JST)
  • Files: TRIS, JSTAGE
  • Created Date: Mar 31 2016 3:04PM