EFFECT OF HEAT CURING HISTORY ON SILICATE STRUCTURES AND HYDRATION OF CEMENT AND SILICA FUME IN ULTRA HIGH STRENGTH CONCRETE

熱養生履歴が超高強度コンクリート中のセメントおよびシリカフュームの水和反応および水和物のケイ酸構造へ与える影響

The influence of heat curing was considered which it has on the hydration and silicate structure of cement paste and silica fume paste. The influences were discussed from the perspectives of cement hydration required by the Rietveld method using powder X-ray diffraction(XRD), silica fume hydration by the selective dissolution method and silicate-chain polymerization of hydrate calcium silicate(C-S-H)by the trimethylsilyl(TMS)derivatization method. The influence of the hydration reaction and silicate structure on a heat curing history was not concerned with the heat curing pattern, but the reaction of cement and silica fume promoted it. In the case of 90℃ highest temperature, the silicate structure more than the trimer of C-S-H increased with cement paste. It checked that more than 90mass% consisted of polymers more than a dimer with silica fume paste.超高強度プレキャストコンクリートの製造を模擬した熱養生履歴がセメントペースト(CP)、シリカフュームペースト(SFP)の水和反応およびケイ酸構造へ与える影響について粉末X線回折/リートベルト法による水和反応解析、SFの反応率、トリメチルシリル誘導体化法によるC-S-Hのケイ酸鎖の重合の観点から考察した。熱養生履歴の水和反応への影響は、熱養生パターンに関わらずセメント、シリカフュームの反応が促進した。ケイ酸構造への影響は、CPでは最高温度90℃でC-S-Hの三量体以上のケイ酸構造が増加し、SFPでは熱養生パターンに関わらず90mass%以上が二量体以上の多量体で構成されていることを確認した。

Language

  • English
  • Japanese

Media Info

Subject/Index Terms

Filing Info

  • Accession Number: 01563243
  • Record Type: Publication
  • Source Agency: Japan Science and Technology Agency (JST)
  • Files: TRIS, JSTAGE
  • Created Date: Apr 23 2015 10:57AM