INFLUENCE OF TITANIUM OXIDE AND MANGANESE OXIDE ON THE MINERAL COMPOSITION AND THE PROPERTIES OF CEMENT

TiO<sub>2</sub>およびMnOがクリンカー鉱物組成およびセメント物性に及ぼす影響

It is expected that minor elements from waste materials, which is used for raw materials of clinker, would cause some impacts on clinker mineral composition and quality of cement. In this study, the authors investigated the influence of TiO₂ and MnO on the clinker mineral composition and the quality of cement. The authors prepared fourteen kinds of clinkers in a laboratory, changing TiO₂ content and MnO content in clinker, respectively. As a result of x-ray diffraction (XRD) Rietveld analysis, the authors identified that TiO₂ decreased alite and ferrite, and increased belite and aluminate. On the other hand, MnO decreased alite and aluminate, and increased belite and ferrite. As a result of mortar compressive strength, both TiO₂ and MnO lowered compressive strength of cement. Because It was estimated that the TiO₂ and MnO decreased alite amount determined by Rietveld analysis. As a result of paste flow, TiO₂ lowered fluidity but MnO improved fluidity. Because it was estimated that TiO₂ and MnO changed aluminate amount determined Rietveld analysis.セメント製造工程では原燃料として廃棄物が使用されているが、廃棄物由来の少量成分がクリンカー中に持ち込まれると、クリンカーの鉱物組成やセメントの物性に影響を及ぼすことが予想される。本研究では、TiO<sub>2</sub>とMnOの含有量の異なる原料を焼成して検討を行った。その結果、TiO₂とMnOがクリンカーの鉱物組成に及ぼす影響はシリケート相では同様の傾向を示し、間隙相では逆の傾向を示すことがわかった。セメントの強度発現性に及ぼす影響はTiO<sub>2</sub>およびMnOを含有することによるエーライト量の変化で概ね整理でき、流動性に及ぼす影響はアルミネート量の変化で整理できることがわかった。

Language

  • English
  • Japanese

Media Info

Subject/Index Terms

Filing Info

  • Accession Number: 01561973
  • Record Type: Publication
  • Source Agency: Japan Science and Technology Agency (JST)
  • Files: TRIS, JSTAGE
  • Created Date: Apr 23 2015 10:50AM