Durability of Combination Type Self Compacting Concrete After Twenty-one-year Exposure

21年間暴露した併用系高流動コンクリートの耐久性

Three large size specimens composed of a combination type self compacting concrete in the range of slump flow 45-76cm were manufactured 21 years ago. The concrete was placed without compaction. These specimens have been exposed to nearshore for 11 years, after that, these were exposed to 20km inland for another 10 years. Then the authors measured the properties of the concretes such as strength, porosity, carbonation depth, and chloride ion diffusivity. As a result, the porosity of the concretes was almost constant depending on neither slump flow nor flow distance. Then, it was found that the combination type self compacting concrete was more durable than conventional concrete with the same W/C. Thus, the carbonation depth of the self compacting concrete was 15-80 percent and the chloride ion diffusion coefficient was 1-10 percent of conventional concrete, respectively.21年前に，スランプフロー45～76cmの範囲で流動性の異なる3つの併用系高流動コンクリートを用いて，それぞれ締固めを行わずに，約6m流動させて大型ブロックを作製した。このブロックを11年間海岸近くに暴露した後，さらに10年間内陸部に暴露し，打設後21年経過したコンクリートの強度，空隙率，中性化深さ，塩化物イオン量などを測定した。その結果，材齢21年の試験体表面部の圧縮強度は流動距離によるばらつきが少ないこと，空隙率はスランプフローや流動距離によらず13～16%とほぼ同じであること，中性化深さは同一水セメント比の普通コンクリートと比較して15～80％程度であること，塩化物イオンの見掛けの拡散係数は同一水セメント比の普通コンクリートと比較して1/10～1/100程度であることが分かった。このことから，併用系高流動コンクリートは普通コンクリートに比べて高い耐久性を有することが確認された。

Language

  • English
  • Japanese

Media Info

Subject/Index Terms

Filing Info

  • Accession Number: 01515535
  • Record Type: Publication
  • Source Agency: Japan Science and Technology Agency (JST)
  • Files: TRIS, JSTAGE
  • Created Date: Feb 24 2014 8:43AM