PREVENTING STRESS CORROSION FAILURES IN SUSCEPTIBLE ALUMINUM ALLOYS
THE MECHANISM OF STRESS CORROSION CRACKING, SUSCEPTIBILITY FACTORS, AND PREVENTION OF STRESS CORROSION IN HIGH- STRENGTH ALUMINUM ALLOYS ARE DISCUSSED. EMPHASIS IS PLACED ON AVOIDING FAILURE BY APPROACHES BASED ON A KNOWLEDGE OF METALLURGICAL STRUCTURE, ENVIRONMENT, AND STRESS DISTRIBUTON. /MPP/
-