PLASTIC SHRINKAGE CRACKING

PLASTIC SHRINKAGE CRACKING OF MORTARS EXPOSED TO DIFFERENT CONDITIONS, AS PREVALENT IN HOT-DRY CLIMATES, WAS INVESTIGATED UNDER CONTROLLED CONDITIONS. THE VARIABLES STUDIED WERE AIR TEMPERATURE AND HUMIDITY, WIND VELOCITY, MORTAR TEMPERATURE, TYPE AND CONTENT OF CEMENT, AND CONSISTENCY. SHRINKAGE, TENSILE STRENGTH AND TENSILE STRESS OF FRESH MORTARS, EVAPORATION AND TIME OF CRACKING WERE MEASURED. WIDTH, DEPTH, AND LENGTH MEASUREMENTS OF THE CRACKS WERE ALSO TAKEN. THE RESULTS CONFIRM THAT RAPID EVAPORATION HAS A PREDOMINANT EFFECT ON PLASTIC SHRINKAGE CRACKING. OTHER CONCLUSIONS ARE THAT PLASTIC SHRINKAGE CRACKING IS NOT A DIRECT FUNCTION OF WATER LOSS, EVAPORATION RATE OR SHRINKAGE, AND THAT SEMIPLASTIC MORTAR DID NOT CRACK UNDER HIGH EVAPORATION CONDITIONS WHICH BROUGHT ABOUT SEVERE CRACKING OF PLASTIC AND WET MORTARS. IT WAS ALSO ESTABLISHED THAT THE FIRST CRACK COINCIDES WITH THE TRANSITION FROM THE INTENSIVE, PRACTICALLY UNRESTRAINED, LINEAR SHRINKAGE OF FRESH MORTAR TO THE MUCH SLOWER RATE DUE TO RESTRAINT ON STIFFENING OF THE MORTAR. /ACI/

• Supplemental Notes:
  • Vol 65, No 4, PP 282-291, 14 FIG, 6 TAB, 9 REF
• Authors:
  • Ravina, D
  • Shalon, R
• Publication Date: 1968-4

Media Info

• Serial:
  • Am Concrete Inst Journal & Proceedings

Subject/Index Terms

• TRT Terms: Cracking; Evaporation; Hot weather construction; Humidity; Mortar; Polymer concrete; Shrinkage; Temperature; Tensile strength; Tension; Velocity; Wind
• Uncontrolled Terms: Tensile stress
• Old TRIS Terms: Shrinkage cracks; Wind velocity
• Subject Areas: Highways; Materials;

Filing Info

• Accession Number: 00212609
• Record Type: Publication
• Files: TRIS
• Created Date: Jun 24 1994 12:00AM